5.3 micron TTR Film
5.3 micron TTR Film
5.3 micron TTR Film
5.3 micron TTR Film

1 / 1

5.3 micron TTR Film

Ontvang de meest recente Prijs
Stuur een aanvraag
Model No. :
Brand Name : SHUANGXING
Material : Polyethylene Terephthalate/PET
Usage : Specialty Plastics
Plastic Properties After Heated : Thermoplastic Plastics
Plastic Forming Method : Extrusion
meer

Product beschrijving

4.5 5.3 mic is the non stop producing thickness of our TTR film

TTR Film Thermal Transfer Ribbon Film


PET Film is made of Polyethylene Terephthalate (PET) for the use as support for ink layers in thermal transfer applications. It is used as base film for thermal transfer ribbons(TTR) in a variety of applications.


It is used as base film for thermal transfer ribbons(TTR) in a variety of applications.

Applications:

- Bar-Code

- Fax machines

- Labeling

- Ticketing

Typical Property:

 

No

Property

Units

Typical Values

Test Values

1

Mechanical

Tensile Strength

MD*

MPa

≥250

385

TD*

MPa

≥200

244

2

Elongation

MD

%

≥80

100

3

TD

%

≥80

143

4

Heat Shrinkage

(150°C,15min)

F5 Value* F5 Value*

MD

%

≤3.5

2.8

TD

%

≤2.5

0.2

W/m.k

0.13

5

Thermal

Heat Shrinkage
(150°C,15min)

A/B-μs*

-

≤0.6

0.44

Thermal conductivity

A/B-μs*

0.38

6

Friction Coefficient

Surface tension

Treated side

mN/m

48

48

*)MD=machine direction TD=transverse direction

*)F5 Value =Tension stress to 5% elongation

*)A/B=untreated side/treated side

Commonly thickness(μm)

Thickness range(%)

Roll length * (m)

Width Specification(mm)

4.5

±6

22000

500-1800

5.2

±6

18000

500-1800

6.0

±5

18000

5001800

Other thickness and lengths on request, Widths on request.
*) Core size 152.4 mm
. The information provided here is consistent with the state of our knowledge at the time of printing, If required please request an up-to-date version of this publication