ASTM A213 gelegeerd stalen buis
| Model No. : | BT09 |
|---|---|
| status : | New |
Product beschrijving
ASTM A213 gespecificeerd voor naadloze ferritische en austenitische ketel-, oververhitter- en warmtewisselaarbuizen van ferritisch en austenitisch gelegeerd staal.
Legeringskwaliteit: T2, T5, T9, T11, T12, T91, T92
Buitendiameter: 28 mm - 168 mm
Wanddikte: 2 mm - 30 mm
ASTM A213 gelegeerd stalen buis chemische samenstelling:
|
Grade |
C |
Mn |
P |
S |
Si |
Cr |
Mo |
V |
N |
Ni |
Al |
Nb |
W |
|
T2 |
0.10-0.20 |
0.30-0.61 |
0.025 max |
0.025 max |
0.10-0.30 |
0.50-0.81 |
0.44-0.65 |
|
|
|
|
|
|
|
T5 |
0.15 max |
0.30-0.60 |
0.025 max |
0.025 max |
0.50 max |
4.00-6.00 |
0.45-0.65 |
|
|
|
|
|
|
|
T9 |
0.15 max |
0.30-0.60 |
0.025 max |
0.025 max |
0.25-1.00 |
8.0-10.0 |
0.90-1.10 |
|
|
|
|
|
|
|
T11 |
0.15 max |
0.30-0.60 |
0.025 max |
0.025 max |
0.50-1.00 |
1.00-1.50 |
0.44-0.65 |
|
|
|
|
|
|
|
T12 |
0.15 max |
0.30-0.60 |
0.025 max |
0.025 max |
0.50-1.00 |
1.00-1.50 |
0.44-0.65 |
|
|
|
|
|
|
|
T22 |
0.05-0.15 |
0.30-0.60 |
0.025 max |
0.025 max |
0.50 max |
1.90-2.60 |
0.87-1.13 |
|
|
|
|
|
|
|
T91 |
0.08-0.12 |
0.30-0.60 |
0.020 max |
0.010 max |
0.20-0.50 |
8.00-9.50 |
0.85-1.05 |
0.18-0.25 |
0.03-0.07 |
0.40 max |
0.04 max |
0.06-0.10 |
|
|
T92 |
0.07-0.13 |
0.30-0.60 |
0.020 max |
0.010 max |
0.50 max |
8.50-9.50 |
0.30-0.60 |
.015-0.25 |
0.03-0.07 |
0.40 max |
0.04 max |
0.04-0.09 |
1.50-2.00 |
ASTM A213 gelegeerd stalen buis mechanische eigenschapstabel:
|
Grade |
Tensile Strength, Mpa |
Yield Strength, Mpa |
Elongation, % |
Hardness, HB |
|
T2 |
415 min |
205 min |
30 min |
163 max |
|
T5 |
415 min |
205 min |
30 min |
163 max |
|
T9 |
415 min |
205 min |
30 min |
179 max |
|
T11 |
415 min |
205 min |
30 min |
179 max |
|
T12 |
415 min |
205 min |
30 min |
179 max |
|
T22 |
415 min |
205 min |
30 min |
163 max |
|
T91 |
585 min |
415 min |
20 min |
250 max |
|
T92 |
585 min |
415 min |
20 min |
250 max |
ASTM A213 gelegeerd stalen buis buitendiameter tolerantie:
|
Method |
Outside Diameter,mm |
Tolerance, mm |
|
Hot Rolled |
OD=101.6 |
+0.4 / -0.8 |
|
101.6<OD=190.5 |
+0.4 / -1.2 |
|
|
190.5<OD=228.6 |
+0.4 / -1.6 |
|
|
Cold Drawn |
OD<25.4 |
±0.10 |
|
25.4=OD=38.1 |
±0.15 |
|
|
38.1<OD<50.8 |
±0.20 |
|
|
50.8=OD<63.5 |
±0.25 |
|
|
63.5=OD<76.2 |
±0.30 |
|
|
76.2=OD=101.6 |
±0.38 |
|
|
101.6<OD=190.5 |
?0.38 / -0.64 |
|
|
190.5<OD=228.6 |
?0.38 / -1.14 |
|
ASTM A213 gelegeerd stalen buis wanddiktetolerantie:
|
Method |
Outside Diameter, mm |
Tolerance, % |
|
Hot Rolled |
OD=101.6,WT=2.4 |
+40 / -0 |
|
OD=101.6,2.4<WT=3.8 |
+35 / -0 |
|
|
OD=101.6,3.8<WT=4.6 |
+33 / -0 |
|
|
OD=101.6,WT>4.6 |
+28 / -0 |
|
|
OD>101.6,2.4<WT=3.8 |
+35 / -0 |
|
|
OD>101.6,3.8<WT=4.6 |
+33 / -0 |
|
|
OD>101.6,WT>4.6 |
+28 / -0 |
|
|
Cold Drawn |
OD=38.1 |
+20 / -0 |
|
OD>38.1 |
+22 / -0 |
|